Quick Details
- Standard: AISI, ASTM, GB, JIS
- Grade: Chemical Composition:, Q345 + Chromium Cabide alloy
- Thickness: 6-30mm, 3+3,6+4,8+6,10+10,12+12,etc
- Place of Origin: Shandong, China (Mainland)
- Brand Name: Zheng Sheng
- Model Number: ZS1000
- Type: Chromium Cabide alloy
- Technique: hardfacing
- Surface Treatment: hardfacing
- Application: Other
- Special Use: Wear Resistant Steel
- Width: 600-1500mm
- Length: 3500mm
- MOQ: 1 piece
- Thickess of alloy layer: 3 - 20mm
- Thickness of base plate: 3 - 20mm
- Hardness: 55 - 65 HRC
- Chromium content: 25 - 40%
- Mounting surface waviness: ≤3mm/1000mm
- History: 10 Years' R&D Experience
- Production Capacity: 200 Sqm per Day
Packaging & Delivery
| Packaging Details | Steel Frame or as require
rizhao zhengsheng chromium carbide overlay hardfacing corrision resisitant wear plate |
|---|---|
| Delivery Time | Shipped in 30 days after payment |
Qingdao chromium steel anti-wear cco abrasion resistant mild steel plate
ZS 1000 Chromium Carbide Overlay Plate
Protect your machinery from wear and reduce maintenance costs with the hardest ,toughest and longest lasting overlay plate around.
Thickness Range : 6-40 mm
Full Sheet Size : 1500 x 3500 mm
1500 x 4500 mm
And we accept customized order.
Wear plate product
| Name | Wear plate |
| Brand | ZHENGSHENG |
| Thickness of base plate | 3mm ~ 20mm |
| Thickness of alloy layer | 3mm ~ 20mm |
| Main thickness | 6-30mm , 3+3,6+4,8+6,10+10,12+12, etc. Customized |
| Hardness | 55 ~ 65HRC |
| Chemical Composition | C:4.0-5.0% Mn: 1.0-5% Cr: 24-45% Fe and others: balance; Actual chemistry will vary with overlay thickness. (Custom chemistries can be developed for specific applications.) |
| Application | 1.Steel Industry 2.Mining Industry 3.Cement and quarry industry 4.Earthmoving machine |
| Advantage | 12-20 times higher than common plate 5-10 times than low alloy steel plate , 2-3 times than high chromium cast iron plate |
ZS1000 Chromium Carbide Overlay Plate
1.The large amount of hard chromium carbides allows this plate to thrive in extreme abrasion and impact applications including wear strips, bucket, blade and truck deck liners, hoppers, shutes and conveyors.
2.The hardness of the overlay plate is a composite of hard chromium carbides, and tough, austenitic matrix. A variety of substrates such as stainless steels, nickel alloys and quenched &
tempered steels, are used in the manufacturing process.
3.This plate can be easily formed to suit curves and contours. Welded studs or countersunk inserts can be fitted so plates become easily replacable.
| Temperature Range | Flatness Tolerance | Microstructure | Characteristics |
1100 degrees Fahrenheit (594 degrees Celsius). Custom chemistries can be developed for higher operating temperatures. | + 1/8” over 5 feet of the length of the plate. This manufacturing specification is crucial when forming and fabricating. | An austenitic matrix with 40-45% hexagonal primary carbides M7C3 & 15-20% blade-like secondary carbides M7C3, along with additional M3C formations. These metallurgical phases are formed during the controlled cooling process as the weld beads are deposited. | The overlay surface of ZS1000 consists of a series of beads with numerous hairline cracks. These properly spaced cracks are a natural stress relief phenomenon and are beneficial to the material. These cracks propagate through the overlay and end the fusion line. |